We are professional manufacturer for aluminium extrusion.

 

About Us

 

Xingxiang Aluminum is a leading aluminium extrusion manufacturer in China since 1992, we also offer complete custom aluminium fabrication services to the needs of our customers.

 

As a experienced aluminium extruder we can deliver large production runs of aluminium profiles, aluminum extrusions, aluminium tubes, aluminum pipes, aluminum round tube, aluminium rectangular tubing, aluminum channels, aluminium window, aluminum door profiles, aluminium heat sink, aluminium solar frame and other custom aluminium extrusion profiles.

 

Also as a skilled metal fabricator, we will provide custom metal fabrication services to our customers. with our fully complete equipment we are capable to manufacture the machined metal parts or a whole completed assembly including surface finishing and packaging to your needs. At Xingxiang Aluminum, we are full equipped and have a large workforce with the desire to be partner with you!

 

Aluminium Extrusion

Material: Aluminium alloy 6063, 6061, 6005, etc.

 

Typical chemical composition for aluminum alloy 6063, 6061 and 6005 (GB/T3190)

Alloy Si Fe Cu Mn Mg Cr Zn T i Impurity Al

6063 0.2-0.6 0-0.35 0-0.1 0- 0.1 0.45-0.9 0-0 .1 0-0.1 0-0.1 0 -0.15 rest

6061 0.4-0.8 0-0.7 0.15-0.4 0-0.15 0.8-1.2 0 .04-0.35 0-0.25 0-0.15 0-0.15 re st

6005 0.6-0.9 0-0.35 0-0.1 0- 0.1 0.4-0.6 0-0. 1 0-0.1 0-0.1 0- 0.15 rest

 

6063-T6 aluminium extrusion

T6 temper 6063 has an ultimate tensile strength of at least 30,000 psi (207 MPa) and yield strength of at least 25,000 psi (172 MPa). In thicknesses of 0.124-inch (3.1 mm) or less, it has elongation of 8% or more; in thicker sections, it has elongation of 10%.

 

6061-T6 aluminium extrusion

T6 temper 6061 has an ultimate tensile strength of at least 42,000 psi (290 MPa) and yield strength of at least 35,000 psi (241 MPa). 

 

Surface finish: Mill finish,Anodizing ,Poder coated, Electrophoresis, etc.

"Mill Finish" is the natural appearnace of the aluminum as it comes from the rolling mill or the aluminum extrusion mill. Aluminum with mill finish has a very lightly oxidized film and will wipe off with your bare finger and immediately form.

 

"Anodizing" is an electrolytic passivation process used to increase the thickness of the natural oxide layer on the surface of aluminum extrusions, ranging may from 0.0003 inches thick on up to 0.003 and on up. Anodizing increases corrosion resistance and wear resistance, also can be used for a number of cosmetic effects.

 

"Powder coating" is a type of coating that is applied as a free-flowing, dry powder. The coating is typically applied electrostaticall y and is then cured under heat to allow it to flow and form a skin.

 

Service

We provide aluminium extrusion, custom fabrication services and technical supports. Feel free to request a quote from Xingxiang Aluminum today!