product name: | AA3004 Aluminium Strip For Lamp Base |
| Place of Origin: | Peoples Republic of China | |
| Post Date: | April 4, 2010 | |
| Edit Date: | May 30, 2022 | |
Detailed Product Description:
Our lamp cap materials combines strength and high formability with high resistance to softening in vitriting. Manufactured at modern and well-equipped mills, it can be rolled to very fine tolerances, allowing more caps per tonne of coil and enabling uninterrupted operations of high-speed forming presses.
| Alloy | 3004 |
| Temper | O |
| Type | Strip Coil |
| Thickness | 0.25-0.40mm |
| Width | 100-500mm |
| Surface Treatment | Mill finish |
| Alloy Or Not | Is Alloy |
| Processing | Direct Casting, Hoting Rolling |
| Features | Good for deep drawing,anodizing |
| Application | Lamp Base Industry |
| Place of Origin | Shandong, China (Mainland) |
| Brand Name | Taixing |
| Model Number | 3004-O |
| metal | aluminum |
|
Alloy |
Si |
Fe |
Cu |
Mn |
Mg |
Cr |
Ni |
Zn |
Ga |
Ti |
Al |
|
3004 |
≤0.3 |
≤0.7 |
≤0.25 |
1.0-1.5 |
0.8-1.3 |
≤0.05 |
≤0.05 |
≤0.25 |
- |
≤0.05 |
other |
|
Alloy |
Temper |
Thickness(mm) |
Width(mm) |
U.T.S(Mpa) |
Elongation(%) |
|
3004 |
O |
0.25-0.40 |
100-500 |
155-200 |
≥13 |
|
Thickness |
Width |
|
±0.01mm |
±0.5mm |
Application: Bulb Caps, Tube Caps, Caps of fluorescent tube lights Electrical Sector, etc
Export Standard Package, moisture-proof, strong enough, suit for long distance sea transport. Lampcap stock is placed on wooden pallets/case in an eye-to-wall position.
AA 3004 is categorized as Wrought Aluminum Alloy. It is composed of (in weight percentage) 97.8% Aluminum (Al), 1.2% Manganese (Mn), and 1.0% Magnesium (Mg). It can be seen in forms of sheet, plate, extruded tubes, and drawn tube. Aluminum is a silverish white metal that has a strong resistance to corrosion and like gold, is rather malleable. It is a relatively light metal compared to metals such as steel, nickel, brass, and copper with a specific gravity of 2.7. Aluminum is easily machinable and can have a wide variety of surface finishes. It also has good electrical and thermal conductivities and is highly reflective to heat and light.
The typical elastic modulus of aluminum alloys at room temperature (25°C) ranges from 70 to 79 GPa. The typical density of aluminum alloys ranges from 2.6 to 2.8 g/cm3. The typical tensile strength varies between 230 and 570 MPa. The wide range of ultimate tensile strength is largely due to different heat treatment conditions
Forming AL 3004 is easily formed by either cold or hot working with conventional tooling.
if your interest it, your can free contact us!